*** LOW
= H04 TS < 60 ksi; MEDIUM= H04 TS 60-75 ksi; HIGH= H04 TS 76-100 ksi; VERY
HIGH= H04 TS > 100 ksi
Performance
Levels: E = Excellent; G = Good; F =
Fair; P = Poor; NR = Not Recommended
|
Alloy UNS
or ACB # |
Composition |
Appearance (Color) |
Conductivity (Electrical & Thermal) % IACS |
Corrosion Resistance |
Cold Forming (Heading, Redrawing, Bending) |
Hot Forming (Forging) |
Joining (Solder) |
Joining (Braze) |
Joining (Arc Weld) |
Tensile Strength (Mechanical Properties) H04 *** |
Machining Machinability Rating FCB = 100 |
Wear Performance |
|
|
CuTe |
COPPER |
93 |
HIGH |
G |
P |
E |
G |
NR |
LOW |
85 |
LOW |
|
19140 19160 |
CuNiPb CuNiPb1 |
COPPER |
55 |
HIGH |
G |
F |
E |
NR |
NR |
HIGH |
75 80 |
LOW |
|
31400 |
CuZn9Pb2 |
RED |
42 |
HIGH |
G |
P |
E |
G |
NR |
MEDIUM |
80 |
LOW |
|
32000 |
CuZn13Pb2 |
RED/YELLOW |
36 |
HIGH |
G |
F |
E |
G |
NR |
MEDIUM |
90 |
LOW |
|
35300 |
CuZn37Pb |
YELLOW |
26 |
LOW |
F |
P |
E |
G |
NR |
MEDIUM |
90 |
LOW |
|
36000,
ACB3601 ACB3602 ACB3605 |
CuZn36Pb3 |
YELLOW |
26 |
LOW |
P |
F |
E |
G |
NR |
MEDIUM |
100 |
LOW |
|
50700 |
CuSn2 |
COPPER |
35 |
HIGH |
E |
G |
E |
E |
G |
MEDIUM |
20 |
MEDIUM |
|
54400 |
CuSn4Zn4Pb4P |
RED |
19 |
HIGH |
G |
P |
E |
G |
NR |
MEDIUM |
80 |
HIGH |
|
6733 |
CuZn34Mn3Si1Pb |
YELLOW |
21 |
LOW |
F |
G |
E |
E |
NR |
HIGH |
65 |
VERY HIGH |
|
67600 |
CuZn38SnFePb |
YELLOW |
24 |
MEDIUM |
P |
G |
E |
E |
F |
HIGH |
60 |
MEDIUM |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
*** LOW
= H04 TS < 60 ksi; MEDIUM= H04 TS 60-75 ksi; HIGH= H04 TS 76-100 ksi; VERY
HIGH= H04 TS > 100 ksi
Performance
Levels: E = Excellent; G = Good; F =
Fair; P = Poor; NR = Not Recommended